Investigation of the weld region of the SAE 1020 joined with metal active gas and determination of the mismatch factor

Meric C., Tokdemir M.

Journal of Materials Engineering and Performance, cilt.8, sa.5, ss.601-605, 1999 (SCI-Expanded, Scopus) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 8 Sayı: 5
  • Basım Tarihi: 1999
  • Doi Numarası: 10.1007/s11665-999-0016-4
  • Dergi Adı: Journal of Materials Engineering and Performance
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.601-605
  • Anahtar Kelimeler: crack tip opening displacement, low carbon steel, metal active gas, mismatch, welding
  • Manisa Celal Bayar Üniversitesi Adresli: Evet

Özet

In this study, the joining process of SAE 1020 low carbon steel, generally used in the industry, has been completed using the metal active gas (MAG) weld method. The goal of this study was to examine the mismatch between base and weld metal. After the joining process, mechanical properties of the samples of the base metal (BM), the heat affected zone (HAZ), and the weld metal (WM) were investigated, and the crack tip opening displacement (CTOD) test was performed.